Search for: All records

Nanoindentation was performed on individual grains of a polycrystalline Mg sample with c-axis declination angles ranging from parallel (0°) to perpendicular (90°) to the c-axis. Hardness was highest at ∼0°, decreased up to ∼55°, and then increased at ∼90° to an intermediate level. At ∼0°, high-density 〈c + a〉 dislocations extended deep into the crystal, contributing to high hardness. At ∼55°, 〈c + a〉 dislocations were confined near the indent, and occasional extension twinning reoriented the crystal to ∼45°, promoting 〈a〉 slip in both matrix and twin, leading to low hardness. At ∼90°, extension twinning reoriented the crystal to ∼0°, inducing texture hardening and intermediate hardness. Despite the complex stress state in nanoindentation, which fundamentally differs from the uniaxial stress in bulk tensile and compression tests, the combined contributions of dislocation and twinning still give rise to measurable hardness anisotropy, suggesting nanoindentation as a high-throughput technique for probing orientation-dependent mechanical behavior in Mg. 

NiTiHf is a class of promising high-temperature shape memory alloys (SMAs) that find many applications. However, their complex martensitic microstructure and attendant thermomechanical properties are not well understood. In this work, we used solution-treated (precipitate-free) and aged (precipitate-bearing) Ni50.3Ti29.7Hf20 (at.%) SMAs as a model system. We observed that the presence of precipitates refines the martensite plates, reduces the number of martensite variants, and changes the orientation relationship between the martensite plates compared with the solution-treated counterpart. Furthermore, the aged samples exhibited higher transformation temperatures, narrower phase transformation temperature windows, improved thermal stability, and retained or even improved actuation strain. The improved thermomechanical properties observed in the aged samples are attributed in part to the reduction of the number of martensite variants and the change in martensite and twin interface characteristics, both of which are induced by the presence of precipitates. The findings of this study offer new information on the processing-property-microstructure relationship in NiTiHf-based SMAs. These insights can guide future materials design efforts, facilitating the development of advanced SMAs tailored for specific high-temperature applications. 

Precession electron diffraction (PED) is a powerful technique for revealing the crystallographic orientation of samples at the nanoscale. However, the quality of orientation indexing is strongly influenced by the quality of diffraction patterns. In this study, we have developed a novel algorithm called Auto-CLAHE (automatic contrast-limited adaptive histogram equalization), which automatically enhances low-intensity diffraction pattern signals using contrast-limited adaptive histogram equalization (CLAHE). The degree of enhancement is dynamically adjusted based on the overall intensity of the diffraction pattern, with greater enhancement applied to patterns with fewer spots (i.e., away from zone axes) and little or no enhancement applied to patterns with many spots (i.e., at a zone axis). By improving the visibility of low-intensity diffraction spots, Auto-CLAHE significantly improves the template matching between experimentally acquired and simulated diffraction patterns, leading to orientation maps with dramatically higher quality and lower noise. We anticipate that Auto-CLAHE provides an efficient and practical solution for preprocessing PED data, enabling higher-quality crystal orientation mapping to be routinely obtained.